Nashik Insulations Resin Glass Banding Tape is a high strength non-woven glass tape used for banding of rotor, armatures and transformer core. It consists of high strength glass yarns laid parallel, impregnated with special high temperature thermosetting polyester resin. During cure, the resin flows and fills the voids and air spaces to produce a homogeneous laminate with a smooth resin surface.
Resin Glass Banding Tape are available in Thermal Class F - 1550C & Thermal Class H - 2000C. Subsequent information is based on widely popular Class H 2000C Banding Tape.
- Thermal Class
- Thermal Rating of Banding
- Yarn Used
- Thicknessof Ends
- Width tolerance
- No of Yarns
- Weight per width
- Tensile Strength B-Stage
- Tensile Strength C-Stage
- Resin Content
- Curing Cycle
- Arc Resistance(ASTM D 495)
Product Offer :
- Width Option
- Length per roll options
- Thermal Class options
Shelf Life Guidelines :
- Shelf Life
- 200oC Max
- E Glass-75 1/2 or equivalent
- 0.3 mm approx
- 30 ±1/cm
- 0.56 kg approx
- ≥ 2000 N/cm
- ≥ 2500 N/cm
- Available from 24% to 30% as per customer requirement
- 5hrs at 150 o C, Once the job reches the temp
- ≥ 120 sec.
- 5, 8, 10, 20, 25, 30, 40, 50, 60, 100
- 100, 200, 1000, 1500, 1800
- Class F-155oC, Class H-200oC, 220oC
- 10, 15, 20, 30
- 24, 18, 12, 8
- As a winding restraint on traction armatures, generators other rotating machines & transformer core binding.
- Other application where high tensile strength and insulating properties of the product can be made use of.
- High Thermal Resistance of upto 200oC. Short period of heating upto 260oC may be tolerated, whereas solder may melt on steel wires.
- Very high Arc Resistance thereby minimizing the possibility of “flash over” which has often been a problem with steel bands.
- Resistant to humidity and corrosion.
- Smooth cured surface on application of banding tape reduces dirt adhesion, which might otherwise lead to tracking failure.
- Non-conducting material, hence eliminates insulation as required under steel banding.
- Prevents Lashing banding tape bands gone far in eliminating the extreme damage caused by lashing wires & lifting armature coils experienced when steel bands break.
- Composite material Banding Tape is subplied in a semi cured soft balanced flat ribbon of glass yarn & high temp. polyester resin. Thus ensuring that each yarn bears a distributed share of load. Banding Tape forms a high strength loop, holds the coil in place against centrifugal forces and has a high safety factor, once suitably applied under requisite winding tension & cured to recommended cycle. Supports weight reduction as compared to steel banding wire.
Due application care is recommended for an optimum performance. It is advised that the banding procedure be standardized on the basis of job & monitored for compliance of process parameters to obtain a desired performance. Generally for the banding tape, in addition to product quality and storage condition, method of use play equally important role on product performance.
Resin Glass Tape should be stored in low temperature atmosphere. See shelf-life guidelines on next page. The tape should be brought back to the ambient condition at the time of use. Except at the time of use it is best to put Banding Tape in plastic cover and seal it to keep clean and to avoid condensation of moisture on the product at low temperature.
Resin Glass Banding Tape require special / quick transportation arrangements. Mutual consultation is suggested for appropriateness depending on transit period, available modes, handling, etc. Considering the sensitivity of Resin Glass Banding Tape promptness is required by the buyer to take delivery of consignment and store suitably.
DOWNLOAD : Resin Glass Banding Tape Application Care